Description
-
Model NO.: NO. 10.67608.0000
-
Shape: U Shaped
-
Temper: T3-T8
-
Alloy: Alloy
-
Alloying Ingredient: 6063
-
Polished Aluminum Profile: Chemical Polishing
-
Colour: Silver,Black,Red,Blue, and Many Other Colors Can B
-
Wall Thickness: Above 0.5mm
-
Trademark: SMC
-
Type: Window & Door Aluminium Profile, Decoration Aluminium Profile, Heat Sink Aluminium Profile, Glass Wall Aluminium Profile, Transport Aluminium Profile
-
Grade: 6000 Series
-
Window & Door Aluminium Profile: 60 Series
-
Surface Finishing: as Customers Required
-
Certification: CE, SONCAP, ISO, CIQ, RoHS, TUV
-
Surface: Mill Finish,Anodized,Eletropharesis,Powder Coated
-
Hardness: MPa≥160,Hv≥58,Hw≥8
-
Oxide Film: AA10,Um10;AA≥15,Um≥15
-
Origin: Shanghai
Specifications of Aluminum T Profile:
1.Grade:6063,6060,6061,6005
2.Temper: T4,T5,T6
3.Surface: Mill Finish,Anodized,Eletropharesis,Powder Coated, Wooden Finish,Polish
4.Certification: ISO 9001:2008;ISO14001:2004;SGS
5.Colour: Silver,Black,Red,Blue, and many other colors can be available
7.Wall thickness:above 0.5mm
8.Hardness:Mpa≥160,HV≥58,HW≥8.
9.Oxide film:AA10,UM10;AA≥15,UM≥15
10.Aluminium profiles deeply processing:cutting,punching,drilling,milling, and fabricating.
Features and Advantages of Aluminum U Profile:
1)Lightweight
2)Good corrosion resistance
3)Weldability
4)Nonmagnetic
5)Greater strength
6)Fine workmanship
7)Good curvature
8)Good appearance
Applications of Aluminum U Profile:
1)Doors and windows
2)Kitchen
3)Equipment frame
4)Industry
5)Curtain wall
6)Solar
7)Decorations
8)Transportation tools
9)Constructions or buildings
etc.
Packaging of Aluminum U Profile:
SMC Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.
Primary Technical Data of Aluminum U Profile:
1)Chemical composition
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Impurity |
Al |
| 6063 |
0.2-0.6 |
0.35 |
0.1 |
0.1 |
0.45-0.9 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
| 6061 |
0.4-0.8 |
0.70 |
0.15-0.4 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.15 |
Rest |
| 6005 |
0.6-0.9 |
0.35 |
0.1 |
0.1 |
0.4-0.6 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
2)Mechanical property
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
| 6061 |
T6 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
| 6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
| T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
3)Anodized
Grade |
Anodizing thickness |
Hole scaling quality of oxide layer |
| Average thickness |
Local thickness |
P. Cr acid-erosion weight less method |
| AA10 |
≥10um |
≥8um |
≤30 mg/d m2 |
| AA15 |
≥15um |
≥12um |
4)Powder coating & wooden-grained
Coating thickness |
Coating impress rigidity |
Adhesive force of coating layer |
| 40-120um |
Indentation hardness>80 |
0 grade |