Description
-
Model NO.: NO. 10.67608.0000
-
Shape: as Customers Required
-
Temper: T3-T8
-
Alloy: Alloy
-
Alloying Ingredient: 6063
-
Polished Aluminum Profile: Chemical Polishing
-
Colour: Silver,Black,Red,Blue, and Many Other Colors Can B
-
Wall Thickness: Above 0.5mm
-
Trademark: SMC
-
Type: Window & Door Aluminium Profile, Decoration Aluminium Profile, Heat Sink Aluminium Profile, Glass Wall Aluminium Profile, Transport Aluminium Profile
-
Grade: 6000 Series
-
Window & Door Aluminium Profile: 60 Series
-
Surface Finishing: as Customers Required
-
Certification: CE, SONCAP, ISO, CIQ, RoHS, TUV
-
Surface: Mill Finish,Anodized,Eletropharesis,Powder Coated
-
Hardness: MPa≥160,Hv≥58,Hw≥8
-
Oxide Film: AA10,Um10;AA≥15,Um≥15
-
Origin: Shanghai
Specifications of Aluminum beam:
1.Grade:6063,6060,6061,6005
2.Surface: Mill Finish,Anodized,Eletropharesis,Powder Coated, Wooden Finish,Polish
3.Shape: I-shape, U-shape,T-shape, Z-shape, or as per the drawings and samples
4.Certification: ISO 9001:2008;ISO14001:2004;SGS
5.Colour: Silver,Black,Red,Blue, and many other colors can be available
6.Temper: T4,T5,T6
7.Wall thickness:above 0.5mm
8.Aluminium profiles deeply processing:cutting,punching,drilling,milling, and fabricating.
Features and Advantages of Aluminum Beam:
1)Lightweight
2)Good corrosion resistance
3)Weldability
4)Nonmagnetic
5)Greater strength
Applications of Aluminum Beam:
1)Decorations
2)Industry
3)Construction/Building, etc.
Primary Technical Data of Aluminum beam:
1)Chemical composition
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Impurity |
Al |
| 6063 |
0.2-0.6 |
0.35 |
0.1 |
0.1 |
0.45-0.9 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
| 6061 |
0.4-0.8 |
0.70 |
0.15-0.4 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.15 |
Rest |
| 6005 |
0.6-0.9 |
0.35 |
0.1 |
0.1 |
0.4-0.6 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
2)Mechanical property
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
| 6061 |
T6 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
| 6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
| T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
3)Anodized
Grade |
Anodizing thickness |
Hole scaling quality of oxide layer |
| Average thickness |
Local thickness |
P. Cr acid-erosion weight less method |
| AA10 |
≥10um |
≥8um |
≤30 mg/d m2 |
| AA15 |
≥15um |
≥12um |
4)Powder coating & wooden-grained
Coating thickness |
Coating impress rigidity |
Adhesive force of coating layer |
| 40-120um |
Indentation hardness>80 |
0 grade |
Packaging of Aluminum beam:
SMC Products are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might be caused during storage or transportation. In addition, clear labels are tagged on the outside of the packages for easy identification of the product I. D. and quality information.
I shape/H shape of Aluminum beam:
Shaped in the form of the letter "I," the I-beam commonly supports floors since it can bear the greatest weight. Also called the "H" beam, it consists of two flat horizontal flanges, one on the top and one on the bottom, that sandwich a vertical beam called the web. The combination of the vertical and horizontal supports equally distribute the weight. Made from aluminum, I-beams are available in many sizes for residential and commercial projects.